AL6082 T6 L bar is a heat-strengthened alloy bar, which has good formability, weldability, machinability, and corrosion resistance. At the same time, it has medium strength and can maintain good operability after annealing. It is mainly used for machinery Structural aspects include bars, plates, pipes and profiles. This alloy has similar but not identical mechanical properties to 6061 alloy, and its -T6 state has higher mechanical properties. Alloy 6082 is a very common alloy product in Europe and has a high application in the United States. It is suitable for processing raw materials, seamless aluminum pipes, structural profiles and custom profiles.
AL6082 T6 L bar usually has good processing characteristics and good anode reaction performance. The most commonly used anode reaction methods include removing impurities and dyeing, coating, etc.
AL6082 T6 L bar combines excellent solderability, brazeability, corrosion resistance, formability and machinability. The 0-0 and T4 states of alloy 6082 are suitable for bending and forming. The -T5 and -T6 states are suitable for good machinability. Some specific processes require the use of chip separators or other special processes to help separate chips. AL6082 T6 L bar usually have good processing characteristics and good anode reaction performance;
AL6082 T6 L bar is widely used in aviation fixtures, trucks, tower buildings, ships, pipelines and other construction applications that require strength, weldability and corrosion resistance. Such as: aircraft parts, camera lenses, couplers, marine accessories and hardware, electronic accessories and connectors, decorative or various hardware, hinge heads, magnetic heads, brake pistons, hydraulic pistons, electrical accessories, valves and valve parts.
Composition of
AL6082 T6 L bar
|
Element |
Si |
Fe |
Cu |
Mn |
Cr |
Mg |
Zn |
Ti |
Al |
|
6082 |
0.7-1.3 |
≤0.5 |
≤0.1 |
0.4-1.0 |
≤0.25 |
0.6-1.2 |
≤0.2 |
≤0.1 |
Rem |
Mechanical properties of
AL6082 T6 L bar According to GB/T 3191-1998
加
Processing |
Temper |
Mpa
Tensile Strength |
Mpa
Yield Strength |
Elongation |
|
Extruded |
T6、T651 |
≥310 |
≥260 |
≥7 |